Poly(3,4-ethylenedioxythiophene), tetramethacrylate end-capped solution 649813-25G

EC Number:	203-572-1
MDL number:	MFCD06798809
NACRES:	NA.23

Please follow this link for Aedotron/Oligotron selection guide table,.
The main characteristic of Oligotron™ PC is that it behaves as a reactive oligomer in non-volatile solvent. Used blended with monomers, or for reactions with functional compounds.
Poly(3,4-ethylenedioxythiophene), tetramethacrylate end-capped solution (PEDOT-Meth) is a semiconductor based polymer that is functionalized with tetramethacrylate that facilitates effective crosslinking of the conjugated films.
For best results, agitate for 20 minutes prior to use. Films cast from propylene carbonate will require heat to dry. Photocurable inks can be formulated by adding acrylate monomers and photoinitiators (i.e. DMPA). Propylene carbonate will remain in the polymer. Functional compounds can be coupled to the oligomer via reactions at the methacrylate group.
PEDOT-Meth can be used as a plasticizing membrane in the fabrication of ion-selective sensors and light emitting diodes.
Product can be blended with additional acrylate or methacrylate monomers and crosslinked to make polymer blends. Custom molecules can be synthesized by bonding functional compounds, via the methacrylate groups, to the conducting EDOT oligomers.
25 g in poly bottle
End-capped structure renders the conducting oligomer PEDOT dispersible. The methacrylate groups offer the potential for crosslinking, or addtional chemical functionalization. Completely dried Oligotron(TM) tetramethacrylate via the methacrylate functional groups.
Store this product at room temperature (do not refrigerate or freeze). Some settling will normally occur. Agitate, sonicate, and filter prior to use. A plug of glass wool in a pipette can be used for easy filtration. The shelf life of this product will vary depending on how it is stored and handled. Product should be discarded if heavy aggregation occurs, or if sonication / filtering are inadequate to produce a good casting solution.
Oligotron is a trademark of TDA Research, Inc.

mol wt	~1,360-1,600 g/mol (methacrylate equivalent weight), average Mn ~6,000(lit.)
Quality Level	100,
contains	p-toluenesulfonate as dopant
composition	Oligotron™ tetramethacrylate, 0.5 wt. % , propylene carbonate, 99.5 wt. %
concentration	0.5 wt. % (dispersion in propylene carbonate)
resistance	1-10 M /sq (typical surface resistance of film)
conductivity	0.1-0.5 S/cm (bulk)
density	1.189 g/mL at 25 °C

pictograms	GHS07
signalword	Warning
hcodes	H319
pcodes	P305 + P351 + P338
RIDADR	NONH for all modes of transport
WGK Germany	WGK 2
Flash Point F	269.6 °F - closed cup
Flash Point C	132 °C - closed cup